Nimonic 901/UNS N09901/2.4662/Alloy 901 Forged Forging Steel Magnesium Copper Brass zinc Extrusion Dies rr manufacturer from China jiangsu liangyi co.,limited

Nimonic 901/UNS N09901/2.4662/Alloy 901 Forged Forging Steel Magnesium Copper Brass zinc Extrusion Dies

Price:	100.0 USD
Payment Terms:	T/T,L/C
Place of Origin:	Jiangsu, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: rr

Production Capacity: 1000 tons

Delivery Date: 60 days

material grade of extrusion Dies: 2.4662

origin of forged extrusion Stems: china

packing: plywooden case

export to country: american european

Means of Transport: Ocean,Air

Packing: plywooden cases

Brand Name: liangyi

size of forged extrusion Dies: as per the drawing

delivery time: 30 days

certificate: API

We are professional Maraging 300/C300/C-300/vascomax 300/1.6358 Forged Forging Steel Magnesium Copper Brass zinc Extrusion Dies

We are professional Nimonic 901/UNS N09901/2.4662/Alloy 901 Forged Forging Steel Magnesium Copper Brass zinc Extrusion Dies from china

Alloy	%	Ni	Cu	Al	Fe	Ti	Co	Mn	S	C	Si	P	Cr	Mo	B
nimonic 901	Min.	40.0				2.35							11.0	5.0	0.01
nimonic 901	Max.	45.0	0.50	0.35	Balance	3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

nimonic 901 Physical properties:

Density	8.14 g/cm3
Melting point	1280-1345℃

nimonic 901 minimum mechanical properties in the room temperature:

Status	Tensile strength Rm N/mm2	Yield strength RP0.2N/mm2	Elongation A5 %
nimonic 901	1034	689	12

Status

Tensile strength Rm N/mm2

Yield strength

RP0.2N/mm2

Elongation

A5 %

nimonic 901

1034

689

Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability

Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before and aging.

Nimonic 901/UNS N09901/2.4662/Alloy 901 Forged Forging Steel Magnesium Copper Brass zinc Extrusion Dies